Isophthalic 3720-L-1 Resin (25kg)
£146.00
SKU: 1160
How To Order Our Products
Chemical/physical nature
Synolite 3720-L-1 is formulated for hand lay-up and spray-up applications. The thixotropic nature of the resin allows application on vertical parts without the risk of sagging or drainage.
Principal properties
Synolite 3720-L-1 is an unsaturated, isophthalic based polyester resin, diluted in styrene. This resin is thixotropic and pre-accelerated.
Product Description
Product specifications
Property Range Unit TM
Solids content, IR 52.0 – 54.0 % 2033
Stability min. 60 minutes 2300C
Viscosity, Physica, 20 s-1, 23?C 450 – 520 mPa.s 2313
Viscosity, Physica, 250 s-1, 23?C 300 – 350 mPa.s 2313
Viscosity, Physica, 50 s-1, 23?C 370 – 430 mPa.s 2313
Gel time from 25 to 35?C 20.0 – 25.0 minutes 2625
Cure time from 25?C to peak 28.0 – 36.0 minutes 2625
Peak temperature 165 – 185 ?C 2625
Remarks
TM 2313: Spindle Z2, 23?C
TM 2625: 2% Butanox M50 by weight
Product specifications
Property Range Unit TM
Tensile E-modulus 2.7 GPa IISO 527-2
Elongation at break 3.5 % ISO 527-2
Tensile strength 60 MPa ISO 527-2
Flexural strength 120 MPa ISO 178
Flexural E-modulus 3.6 GPa ISO 178
Heat Deflection Temp. (HDT) 105 ?C ISO 74-A
Properties of the liquid resin (typical values)
Properties of the liquid resin (typical values)
Property Value Unit TM
Flash point appr. 33 ?C 2800
Stability, no init., dark,
20?C
3 months –
Guidelines before use
Before use, the resin should be conditioned at a well defined, application dependent temperature (usually15?C minimum for a MEKP / Co cure). Ensure the product is thoroughly stirred before use.
Storage guidelines
The resin should be stored in the original, unopened and undamaged packaging, in a dry place at temperatures between 5?C and 30?C. Shelf life is reduced at higher temperatures. The shelf life of styrene containing unsaturated polyesters will be significantly reduced when exposed to sunlight. Store in dark and in 100% light tight containers only.
Additional information
Weight | 25 kg |
---|